Controlled rheology polypropylene heterophasic copolymers

ABSTRACT

This invention relates to the use of a cyclic ketone peroxide of half-life time larger than one second at a temperature of 225° C., for producing a controlled rheology polypropylene heterophasic copolymer of melt index MI2 larger than 15 g/10 min, having simultaneously a very high impact resistance and a high flexural modulus.

The present invention relates to polypropylene heterophasic copolymers modified with cyclic ketone peroxides in order to better control their impact strength.

Several processes for increasing the impact strength of polypropylene (co)polymers are known in the art, for example, by modifying said (co)polymers with elastomeric modifiers or with peroxides.

Where elastomeric modifier is used to modify the (co)polymers, it can be added in either of the following ways:

-   -   reactor polymerisation of polypropylene heterophasic copolymers.         These polypropylene heterophasic copolymers exhibit typical         heterophasic morphology consisting of ethylene propylene         bipolymer spherical domains dispersed in a semi-crystalline         polypropylene matrix. This material consists generally of three         components: a polypropylene homopolymer, a rubbery ethylene         propylene bipolymer and a crystalline ethylene-rich ethylene         propylene bipolymer. The amount and properties of the three         component material are controlled by the process conditions. The         mechanical properties of the final product are influenced for         example by:     -   1. the molecular weight, molecular weight distribution and         tacticity of the propylene homopolymer matrix;     -   2. the molecular weight and molecular weight distribution of the         ethylene propylene rubber phase;     -   3. the ethylene/propylene ratio of the ethylene propylene rubber         phase;     -   4. the content and dispersion of the optional ethylene rich         ethylene propylene bipolymer;     -   5. the size and distribution of the rubber phase domains;     -   6. the melt viscosity ratio of the propylene matrix and rubber         phase components.     -   Melt blending polypropylene (co)polymers with elastomeric         modifiers to prepare polypropylene heterophasic copolymers.         Elastomers such as ethylene propylene rubber (EPR) or ethylene         propylene diene monomer (EPDM) provide improved impact         behaviour. The impact resistance of these compositions depends         upon the content, the composition and the morphology of the         elastomeric modifier.

Both methods have been described for example in: Polypropylene, structure, blends and composites. Volume 2—Copolymers and blends. Edited by J. Karger-Kocsis, Published in 1995 by Chapman § Hall.

WO-95/11938 discloses a process of modifying (co)polymers by contacting them with a peroxide compound containing an activated unsaturated group and an acid group in the presence of a polymer reinforcing material, or prior to the addition of a polymer reinforcing material. The primary object of that invention was to modify (co)polymers in order to introduce an adhesion promoting functional group and to improve their properties. The resulting modified (co)polymers have improved impact strength, flexural strength, tensile strength and elongation at break, increased melt flow index and the other properties equal those of the unmodified impact (co)polymers.

WO-97/49759 discloses a process for enhancing the melt strength of a propylene (co)polymer by the steps of:

-   -   mixing an initiator with the propylene (co)polymer at a         temperature below the decomposition temperature;     -   then heating the mixture above the initiator decomposition         temperature in order to decompose the initiator before the         polymer has melted and in order to react the radicals created by         the decomposition with the polymer.

WO-96/03444 discloses a process for modifying (co)polymers by contacting these with an organic peroxide, some of said peroxide being decomposed. Cyclic ketone peroxides have been found particularly efficient in the modification processes. They have been employed in the degradation of polyolefins, the cross-linking of polyolefins, the dynamic cross-linking of blends of elastomers and thermoplastic polymers, the grafting of monomers onto polymers, or the functionalisation of polyolefins. The resulting modified (co)polymers had a larger melt flow index, a lower weight average molecular weight and a narrower molecular weight than the starting (co)polymers, while keeping an adequate melt strength.

WO-00/23434 discloses a composition comprising a cyclic ketone peroxide and a phlegmatizer having a 95% boil-off point falling in the range of 220-265° C. Preferably, the peroxide is a cyclic ethyl ketone peroxide and a single phlegmatiser is used.

U.S. Pat. No. 4,707,524 discloses the use of peroxides that do not decompose to tert-butyl alcohol and have a half-life in the range of 1 to 10 hours at 128° C. for controlling the molecular weight and molecular weight distribution of polypropylene.

WO-96/03397 discloses a transportable, storage stable ketone peroxide composition which comprises 1 to 90 wt % of one or more cyclic ketone peroxides and 10 to 99 wt % of one or more diluents selected from the group consisting of liquid phlegmatisers for the cyclic ketone peroxides, plasticisers, solid polymeric carriers, inorganic supports, organic peroxides and mixtures thereof.

WO-96/20247 discloses cross-linked polymer compositions of propylene-ethylene copolymer and ethylene-α-olefin copolymer prepared by melting and kneading the constituents in the presence of a radical forming agent, a cross-linking agent and eventually a peroxide inhibitor. These compositions were characterised by a high impact strength and a high flexural modulus.

EP-0,208,330 discloses a propylene polymer composition with increased whitening resistance and increased impact strength, obtained by addition of an ester, in the presence of a peroxide, during extrusion.

None of these prior art documents discloses polypropylene heterophasic copolymers having simultaneously a melt flow index MI2 larger than 15 g/10 min and increased impact strength, while keeping adequate rigidity.

It is an aim of the present invention to provide polypropylene heterophasic copolymers exhibiting simultaneously high melt flow index and high impact strength.

It is another aim of the present invention to provide polypropylene heterophasic copolymers with very high impact resistance over a large range of temperatures.

It is a further aim of the present invention to obtain polypropylene heterophasic copolymers with controlled rheology.

It is yet another aim of the present invention to obtain a material with an optimal balance of stiffness, impact strength and melt flow.

This invention discloses a polypropylene (co)polymer degraded with a cyclic ketone peroxide characterised in that it retains an Izod notched impact strength for melt flow indices larger than 15 g/10 min that is at least 50% higher than that of a polypropylene (co)polymer degraded with a linear peroxide under similar conditions.

Preferably, the impact strength of the degraded polypropylene (co)polymer of the present invention retains an Izod notched impact strength that is twice as large as that of the prior art resins.

This invention also discloses the use of cyclic ketone peroxide, to degrade a polypropylene (co)polymer, for producing a controlled rheology material of melt index MI2 larger than 15 g/10 min, said impact propylene copolymer having simultaneously an impact resistance that is at least 50% higher and a flexural modulus that is 30 Mpa higher than those of the polypropylene (co)polymers degraded with linear peroxides under similar conditions.

The half-life time of the cyclic ketone peroxides of the present invention is typically longer than one second at a temperature of 225° C., preferably it is of from 2 to 10 seconds at a temperature of 225° C., and most preferably, it is about 4 seconds at a temperature of 225° C.

The half-life time of peroxide is defined as the time required to decompose one half of the molecules at a given temperature, and thus a less reactive peroxide has a longer half-life time. A longer half-life time has two favourable consequences:

-   -   1. the peroxide decomposes more slowly; there is thus more time         for mixing with the polymer melt in the extruder resulting in a         more homogeneous material;     -   2. there is at any time a lower radical concentration, reducing         the probability of side reactions.

Reducing the extrusion temperature increases the half-life time of the peroxide.

The melt index MI2 is measured using the method of standard test ISO 1133 at 230° C. and under a load of 2.16 kg, the flexural modulus is measured using the method of standard test ISO 178 and the impact strength is the Izod notched impact strength measured according to the methods of standard test ISO 180.

The process for preparing a controlled rheology polypropylene heterophasic copolymer by degrading a polypropylene with a cyclic ketone peroxide, comprises the steps of:

either

-   -   a) Reactor polymerising a polypropylene heterophasic copolymer;     -   b) Extruding the polypropylene heterophasic copolymer of step         a), with said cyclic ketone peroxide and optionally with one or         more filler(s), in an extruder, at a temperature sufficient to         maintain the copolymer in the molten state;         Or     -   c) Extruding a polypropylene (co)polymer with said cyclic ketone         peroxides, and optionally, with one or more elastomeric         modifier(s) and/or one or more filler(s), in an extruder, at a         temperature sufficient to maintain the copolymer in the molten         state.

The specific group of cyclic ketone peroxide of half-life time longer than one second at a temperature of 225° C., can be represented by either of the general formulae:

Wherein R₁-R₁₀ are independently selected from the group consisting of hydrogen, C₁-C₂₀ alkyl, C₃-C₂₀ cycloalkyl, C₆-C₂₀ aryl, C₇-C₂₀ aralkyl, C₇-C₂₀ alkaryl, which groups may include linear or branched alkyl moieties; and each of R₁-R₁₀ may be optionally substituted with one or more groups selected from hydroxy, C₁-C₂₀ alkoxy, linear or branched C₁-C₂₀ alkyl, C₆-C₂₀ aryloxy, halogen, ester carboxy, nitrile, and amino.

Preferably, the peroxide is a cyclic peroxide containing at least two peroxide goups, and most preferably, it is 3,6,9-triethyl-3,6,9-trimethyl-1,4,7-triperoxonane. The latter molecule has three peroxide groups and a relatively small number of carbon atoms and thus a level of active oxygen of the order of 18.16 wt %.

The treatment of a polypropylene with peroxide generally produces a modified polymer by creation of functional groups. Peroxide radicals can cause chain scission and/or cross-linking, resulting in an increase of the melt flow index. It must be noted however that increasing the degradation ratio causes a decrease of the flexural modulus. The amount of peroxide necessary to carry out the invention depends upon the chemical nature of the peroxide, upon the starting melt flow index and upon the desired final melt flow index: it is directly proportional to the final melt flow index. Melt flow index of from 2 to 70 g/10 min have been obtained, but the efforts of the present invention are focused on products having a melt flow index larger than 15 g/10 min. The main departure from the strength and stiffness behaviour of prior art materials occurs for resins having a melt flow index above 15 g/10 min.

In a preferred embodiment of the present invention, the polypropylene heterophasic copolymer is prepared by copolymerising propylene with ethylene in the proportions of from 5 to 20 wt % of ethylene and 95 to 80 wt % of propylene. The copolymerisation is effected in two reactors as follows:

-   -   a) the catalyst and propylene are charged into a first loop         reactor equipped with a circulation pump, at a temperature of         from 60 to 80° C. and under a pressure of from 35 to 40 bars,         using the liquid monomer as a suspension vehicle, in order to         produce a homopolymer of propylene on the surface of the         catalyst grains;     -   b) the polymer-coated catalyst grains are transferred to one or         more secondary gas phase reactors with a fluidised bed and         ethylene is added in order to produce an ethylene-propylene         rubber.

The polypropylene heterophasic copolymer so obtained has a typical heterophasic morphology consisting of ethylene-propylene bipolymer spherical domains dispersed in a semi-crystalline polypropylene matrix. These materials generally consist of three components: a propylene homopolymer, a rubbery ethylene-propylene bipolymer and a crystalline ethylene-rich ethylene-propylene bipolymer. The amount and properties of the components are controlled by the process conditions and the physical properties of the resulting material are correlated to the nature and amount of the three components. In the present invention, the preferred amount of ethylene is of from 9 to 15 wt % and more preferably, it is from 11 to 14 wt %.

The polypropylene heterophasic copolymer is then extruded in an extruder with a cyclic ketone peroxide and with one or more optional fillers, such as glass fillers, talc, calcium carbonate or clay minerals. The cyclic ketone peroxide has a half-life time longer than one second at a temperature of 225° C. The extrusion is carried out at a temperature sufficient to maintain the material in a molten state. In the examples carried out with the preferred peroxide of the present invention, the extrusion temperatures are from 160° C. up to less than 200° C., preferably from 160 to 190° C. The resin obtained after degradation of the polypropylene (co)polymer at low temperature exhibit an excellent impact performance. That result is totally unexpected as it is generally known in the art to work at temperatures higher than 200° C. with long half-life time peroxides, in order to compensate for their low reactivity level. It must be noted in addition that the resins prepared according to the present invention retain higher impact strength than prior art resins, for extrusion temperatures higher than 200° C.

The Izod notched impact strength of the final resin depends upon the amount of ethylene present in the polypropylene heterophasic copolymer: it increases with increasing amounts of ethylene. The rigidity, on the contrary, decreases with increasing amounts of ethylene, thereby imposing an upper limit to the amount of ethylene incorporated into the copolymer.

It is further observed, that the final resins obtained according to the present invention, when extruded at cold temperature, retain an Izod notched impact strength at 23° C. above 40 kJ/m², for melt flow indices ranging from 15 to 40 g/10 min and for an ethylene content of from 9 to 15 wt % in the polypropylene heterophasic copolymer. For an ethylene content in the polypropylene heterophasic copolymer larger than 12 wt % and an extrusion temperature of at most 200° C., the impact strength of the compositions according to the present invention remains above 40 kJ/m² for melt flow indices up to 70 g/10 min. Throughout this disclosure, cold extrusion temperature is understood as a temperature ranging from the temperature at which all components are in the molten state up to a temperature of less than 200° C.

In addition, it is also observed that both the extrusion temperature and the percentage of ethylene contained in the polypropylene heterophasic copolymer have an influence on the behaviour of the Izod notched impact strength as a function of melt flow index. Decreasing the extrusion temperature or increasing the amount of ethylene results in final resins that retain the impact properties at values of the melt flow index larger than 40 g/10 min. It is thus possible, playing with these two parameters to tailor the desired final resins.

The copolymers of the present invention are used in several applications that require simultaneously a melt flow index larger than 15 g/10 min, high impact strength and high flexural modulus such as for example: crates, ice cream containers, yoghurt beakers, storage bins, suitcases, lids, pails, technical parts, garden articles, automotive parts, batteries, thin wall packaging, medical waste containers and compounds. Compounds are particularly valuable as they allow the production of articles with less or no elastomeric modifiers thereby allowing reduction of cost and processing time.

LIST OF FIGURES

FIG. 1 represents a plot of the Izod notched impact strength at 23° C., expressed in kJ/m², as a function of the melt flow index, expressed in g/10 min, for an ethylene content in the polypropylene heterophasic copolymer of 11.3 wt % and for an extrusion temperature of 200° C.

FIG. 2 represents a plot of the Izod notched impact strength at 23° C., expressed in kJ/m² as a function of the melt flow index, expressed in g/10 min, for an ethylene content in the polypropylene heterophasic copolymer of 11.3 wt % and for extrusion temperatures of 160° C. and of 200° C.

FIG. 3 represents a plot of the Izod notched impact strength at 23° C., expressed in kJ/m², as a function of the melt flow index, expressed in g/10 min, for an ethylene content in the polypropylene heterophasic copolymer of 13.2 wt % and for an extrusion temperature of 200° C.

FIG. 4 represents a plot of the Izod notched impact strength at 10° C., expressed in kJ/m², as a function of the melt flow index, expressed in g/10 min, for an ethylene content in the polypropylene heterophasic copolymer of 13.2 wt % and for an extrusion temperature of 200° C.

FIG. 5 represents a plot of the Izod notched impact strength at 23° C., expressed in kJ/m², as a function of the melt flow index, expressed in g/10 min, for ethylene contents in the polypropylene heterophasic copolymer of 11.3 and of 13.2 wt %, and for an extrusion temperature of 200° C.

EXAMPLE 1

Several samples have been prepared using as starting material a polypropylene heterophasic copolymer having a melt flow value MI2 of 2 g/10 min and an ethylene content of 11.3 wt %. The polypropylene heterophasic copolymer has been extruded in a single-screw Gloenco extruder, at a temperature of 200° C., with various amounts of the cyclic peroxide 3,6,9-triethyl-3,6,9-trimethyl-1,4,7-triperoxonane in a 41.3% solution of Isopar M diluent and having 7.5 wt % of active oxygen, in order to obtain the desired melt flow index for the finished material. The formulation of these materials contains in addition Irganox and Irgafos as antioxidants, 400 ppm of calcium stearate, 3500 ppm of talc and 2000 ppm of glycerol monostearate (GMS) as antistatic agent. The data are summarised in Table I. TABLE I Cyclic peroxide consumption (ppm) Final MFI (g/10′) 350 7.2 700 12 900 24.7 1380 37.9 1810 56 2110 73.4

The flexural modulus has been measured at 23° C. using the method of standard test ISO 178 and the Izod notched impact strength has been measured at 23° C. using the method of standard test ISO 180. The results are summarised in Table II and in FIG. 1.

COMPARATIVE EXAMPLES

The same polypropylene heterophasic copolymer as that used hereabove has been extruded with various amounts of 2,5-bis(tert-butylperoxy)-2,5-dimethylhexane sold by Akzo Nobel. Chemicals B.V. under the trade-name Trigonox 101 under the same conditions as in Example 1. The amounts of peroxide have been adjusted in order to produce finished materials with comparable melt flow indices of respectively 8, 12, 27.2, 38.2, 63.5 and 74, as those of the samples according to the invention. The amounts of peroxide consumed are respectively 250, 500, 800, 1060, 1390 and 1650 ppm. The flexural modulus and Izod notched impact strength are also presented in Table II and FIG. 1 for comparison. TABLE II Perox. 101* cycl* 101 cycl 101 cycl 101 cycl 101 cycl 101 cycl MFI 8 7.2 12 12 27.2 24.7 38.2 37.9 63.5 56 74 73.4 g/10′ Flex. 1160 1216 1050 1120 1040 1065 1000 1036 965 1000 945 995 Mod. Mpa Izod 56.5 60.7 19 54 20.7 51 13.2 21.1 12.7 15.1 11.7 14.3 23° C. kJ/m² *101 = Trigonox 101 and cycl = 3,6,9-triethyl-3,6,9-trimethyl-1,4,7-triperoxonane.

From Table II and FIG. 1, it appears that the material produced according to the present invention has a flexural modulus that is larger by about 40 MPa than that of the material produced with Trigonox 101 for melt indices larger than 15 g/10 min.

From Table II and FIG. 1, it is observed that the Izod notched impact strength at 23° C., of the material produced according to the present invention, quite unexpectedly does not decrease sharply for a melt flow index larger than 15 g/10 min as does the material prepared with Trigonox 101. It remains fairly high up to a value of the melt index of about 40 g/10 min. Above that value, it remains significantly higher than that of the comparative samples.

EXAMPLE 2

The Izod notched impact strength has been measured, at the temperatures 23, 10 and −20° C., for melt indices of 12, 25 and 40, for extrusion temperatures of 160, 180 and 200° C. and for two peroxides. The controlled rheology polypropylene heterophasic copolymer samples according to the present invention have been prepared with an ethylene content of 11.3 wt % and with the same cyclic ketone peroxide as that used in example 1. The comparative examples have been prepared with the linear peroxide sold by Akzo Nobel Chemicals B.V. under the name Trigonox 101. The results are summarised in Table III and in FIG. 2. TABLE III Izod notched impact strength (kJ/m²) at 23° C., 10° C. and −20° C. Ex. T. = 200° C. Ex. T. = 180° C. Ex. T. = 160° C. Peroxide MFI 23 10 −20 23 10 −20 23 10 −20 101 12 19 na 6 45* 13 6 47* 13 6 101 25 20 na 8 32** 10 6 24** 10 6 101 40 13 na 7 14  8 5 14  9 5 cyclic 12 54* na 7 51*  43* 6 52*  42* 7 cyclic 25 51* na 7 48* 13 6 46* 13 6 Cyclic 40 21 na 8 45* 11 6 45* 11 6 na: not available *no break **no break of some samples

It can be concluded from these results that the material prepared according to the present invention has an impact strength that is superior to that of the comparative samples, in all cases. The results are particularly remarkable at low extrusion temperatures of 160 and 180° C.

EXAMPLE 3

Controlled rheology resins were prepared based on the MI2=2 g/10 min (ISO 1133) reactor polymerised polypropylene heterophasic copolymer with an ethylene content of 13.2%. Anti-oxidants, calcium stearate (400 ppm), nucleation (talc 3500 ppm) and antistatic agents (glycerol monostearate (GMS) 90% 2000 ppm) were added during extrusion on a single screw Gloenco extruder. Two different peroxide were used: 2,5-di-tert-butyl-2,5-dimethylhexyl peroxide sold by Akzo Nobel Chemicals B.V. under the trade-name Trigonox 101 and 3,6,9-Triethyl-3,6,9-Trimethyl-1,4,7-triperoxonane.

The degradation ratios were of 6, 12.5 and 20 and the extrusion temperature was 200° C. Melt flow index, flexural modulus and Izod notched impact strength are reported in Table IV. The Izod notched impact strength results are also summarised on FIGS. 3, 4 and 5 for temperatures of +23° C. and +10° C. respectively. TABLE 4 Tr. 101 cyclic Tr. 101 cyclic Tr. 101 Cyclic Tr. 101 Cyclic Property Start MFI 12 MFI 12 MFI 25 MFI 25 MFI 40 MFI 40 MFI 70 MFI 70 MFI (g/10 min) 2.4 11.3 11.3 24.3 23.0 39.0 39.2 70 70 Flexural Modulus 1130 1040 1035 990 995 925 980 (MPa) Izod Notched +23° C. 57.7* 49.4* 54.2* 43.1* 48.7* 14.5 41.7* 14 41 (kJ/m²) Izod Notched +10° C. 50.1* 16.0 48.3** 10.3 27.4** 12.1 11.9 (kJ/m²) Izod Notched −20° C. 7.5 6.4 6.6 5.6 6.2 5.7 4.9 (kJ/m²) *no-break **no-break of some samples.

All the resins produced with both the linear and cyclic peroxides at an extrusion temperature of 200° C. and for melt flow index of from 12 to 25 g/10 min show ‘no break’ at room temperature. This in contrast to the results obtained in the previous example prepared by degrading a polypropylene heterophasic copolymer with a lower ethylene content. A higher ethylene content (13.2 vs. 11.3%) thus drastically improves the impact performance of polypropylene heterophasic copolymers.

Changing the peroxide type from linear (Trigonox 101) to cyclic improves the ‘no break’ performance of the final resin with a melt flow index of 70 g/10 min at a temperature of 23° C.

The resins having a melt flow index of 12 and of 25 g/10 min produced with the cyclic ketone peroxide also show excellent impact performance at a temperature of 10° C.

From these examples, it can be concluded that the cyclic ketone peroxide offers an important mechanical advantage over the linear peroxide Trigonox 101.

-   -   It is possible to produce better flow materials that keep their         impact strength for a melt flow index as high 70 g/10 min and         show ‘no-break’ from an Izod notched impact test at room         temperature. The materials also show a better impact performance         at other temperatures.     -   In almost all cases the flexural modulus is higher.

In conclusion, the resins produced according to the present invention exhibit an improved balance of stiffness, impact, strength and flow properties. The materials produced according to the present invention are thus particularly useful for preparing articles that require simultaneously high melt flow and good impact strength. Indeed high melt flow material is easier and faster to process, particularly in injection moulding, thus allowing shorter cycle time and reduction of the walls' thickness while keeping an acceptable stiffness and impact strength. 

1. A polymer composition produced by the process of degrading a polypropylene (co)polymer with a cyclic ketone peroxide, said polymer composition characterized by an Izod notched impact strength for melt flow indices greater than 15 g/10 min that is at least 50% higher than the Izod notched impact strength for melt flow indices greater than 15 g/10 min of a comparative polymer composition produced by degrading said propylene (co)polymer with a linear peroxide under the same conditions of degrading.
 2. The polymer composition of claim 1 produced by degrading a polypropylene (co)polymer that looses its impact strength when the melt flow index reaches a threshold value that increases with decreasing extrusion temperature.
 3. The polymer composition of claim 1 produced by degrading said polypropylene (co)polymer in the presence of a cyclic ketone peroxide having at least two peroxide groups.
 4. The polymer composition of claim 3 produced by degrading said propylene (co)polymer with 3,6,9-triethyl-3,6,9-trimethyl-1,4,7-triperoxonane.
 5. The polymer composition of claim 3 wherein the propylene (co)polymer is degraded by extrusion at a temperature of from 160° C. to less than 200° C.
 6. The polymer composition of claim 1 produced by degrading a polypropylene heterophasic copolymer, containing from 5 to 20 wt % of ethylene.
 7. The polymer composition of claim 6 produced by degrading a polypropylene heterophasic copolymer containing from 9 to 15 wt % of ethylene.
 8. The polymer composition of claim 6 produced by degrading a copolymer that looses its impact strength when the melt flow index reaches a threshold value that increases with increasing amount of ethylene.
 9. The polymer composition of claim 1 characterized by an Izod notched impact strength that is at least twice that of the Izod notched impact strength of said comparative polymer composition.
 10. The polymer composition of claim 1 characterized by a flexural modulus that is at least 30 Mpa higher than the flexural modulus of said comparative polymer composition.
 11. A method of degrading a polypropylene (co)polymer which comprises extruding said polypropylene (co)polymer with a cyclic ketone peroxide to form a solid product of said polypropylene (co)polymer having a melt index greater than 15 g/10 min with an Izod notched impact strength that is at least 50% higher and a flexural modulus that is at least 30 Mpa higher than the Izod notched impact strength and flexural modulus of a corresponding polypropylene (co)polymer degraded with a linear peroxide under similar conditions.
 12. The method of claim 11 wherein said extrusion is carried out at an extrusion temperature of 200° C. or less.
 13. The method of claim 11 wherein said cyclic ketone peroxide has a half-life of more than one second at a temperature of 225° C.
 14. The method of claim 11 wherein said cyclic ketone peroxide has a half-life of from two to 10 seconds at a temperature of 225° C.
 15. The method of claim 11 wherein said extrusion is carried out at a temperature of from 160° C. to less than 200° C.
 16. The method of claim 15, wherein the polypropylene (co)polymer is a polypropylene heterophasic copolymer containing from 5 to 20 wt % of ethylene.
 17. The method of claim 11 wherein said polypropylene (co)polymer is a polypropylene heterophasic copolymer containing ethylene in an amount within the range of 9-15 wt %.
 18. The method of claim 17 wherein said polypropylene heterophasic copolymer contains from 11 to 14 wt % ethylene.
 19. The method of claim 11 wherein the extrusion temperature is within the range of 160-190° C.
 20. The method of claim 11 wherein said cyclic ketone peroxide is 3,6,9-triethyl-3,6,9-trimethyl-1,4,7-triperoxonane. 